International Standard  ISO 6508-1:2015(E) 

Metallic materials — Rockwell hardness test — 

Part 1: 

Test method

ISO 6508 consists of the following parts under the general title Metallic materials —— Rockwell hardness test:

ISO 6508-1 Metallic materials —— Rockwell hardness test Part 1: Test method

ISO 6508-2 Metallic materials —— Rockwell hardness test Part 2: Verification and calibration of testing machines and indenters

ISO 6508-3 Metallic materials —— Rockwell hardness test Part 3: Calibration of refernce blocks

Content

Foreword 
1 Scope
2 Normative references
3 Principle
4 Symbols, abbreviated terms and designations
5 Testing machine
6 Test piece
7 Procedure
8 Uncertainty of the results
9 Test report
10 Conversions to other hardness scales or tensile strength values
Annex A (normative) Special HR30TSm and HR15TSm test for thin products
Annex B (normative) Minimum thickness of the test piece in relation to the Rockwell hardness
Annex C (normative) Corrections to be added to Rockwell hardness values obtained on 

            convex cylindrical surfaces
Annex D (normative) Corrections to be added to Rockwell hardness C scale values obtained 

            on spherical test surfaces of various diameters
Annex E (normative) Daily Verification Procedure
Annex F (normative) Inspection of diamond indenters
Annex G (informative) Uncertainty of the measured hardness values
Annex H (informative) CCM - Working Group on Hardness
Annex I (informative) Rockwell Hardness Measurement Traceability
Bibliography


1  Scope

This part of ISO 6508 specifies the method for Rockwell regular and Rockwell superficial hardness tests
(scales and applicable range of application according to Table 1) for metallic materials and is applicable
to stationary and portable hardness testing machines.

For specific materials and/or products, other specific International Standards apply (for instance,

ISO 3738-1 and ISO 4498).

NOTE Attention is drawn to the fact that the use of tungsten carbide composite for ball indenters is 

considered to be the standard type of Rockwell indenter ball. Steel indenter balls are allowed to continue

to be used only when complying with Annex A.


2  Normative references

The following documents, in whole or in part, are normatively referenced in this document and are
indispensable for its application. For dated references, only the edition cited applies. For undated
references, the latest edition of the referenced document (including any amendments) applies.

ISO 6508-2:2015，Metallic materials — Rockwell hardness test — Part 2: Verification and calibration of
testing machines
ISO 6508-3:2015，Metallic materials — Rockwell hardness test — Part 3: Calibration of reference blocks

相关标准

国家标准GB/T 230.1-2018《金属材料 洛氏硬度试验 第1部分：试验方法》

       本标准修改采用国际标准ISO6508-1:2005《金属材料 洛氏硬度试验 第1部分:试验方法(A、B、C、D、E、F、G、H、K、N、T 标尺)》(英文版)。 

       本标准根据ISO6508-1:2005重新起草,根据我国的实际情况,本标准在采用国际标准时进行了修改和补充。这些技术性差异用垂直单线标识在它们所涉及的条款的页边空白处。 

       本标准结构和技术内容与ISO6508-1:2005基本一致,根据我国情况在以下几方面进行了修改: 

       —— 删去了国际标准的前言; 

       —— 删除了引言; 

       —— 本国际标准一词改为本标准; 

       —— 用小数点.代替作为小数点的,; 

       —— 增加了对试样表面粗糙度的建议; 

       —— 增加了试验结果有效位数的规定; 

       —— 修改了附录G 洛氏硬度测量值的不确定度分析方法。